产品描述
锻造钢球广泛应用于水泥、矿山、电厂、化学等工业。锻球抗冲击性好、韧性强、耐磨性好、不易破碎和失圆。可提高球磨机的生产力，降低生产成本。
化学成分
化学成分
| C | Mn | Si | Cr | S | P |
50MN | 0.48-0.56 | 0.70-1.0 | 0.17-0.37 | ≤0.25 | ≤0.035 | ≤0.035 |
60MN | 0.57-0.65 | 0.50-0.80 | 0.17-0.37 | ≤0.25 | ≤0.035 | ≤0.035 |
65MN | 0.62-0.70 | 0.90-1.20 | 0.17-0.37 | ≤0.25 | ≤0.035 | ≤0.035 |
75Mn | 0.72-0.92 | 0.70-1.20 | 0.17-0.37 | 0.4-0.6 | ≤0.035 | ≤0.035 |
75MnCr | 0.70-0.85 | 0.70-0.80 | 0.17-0.37 | 0.2-0.7 | ≤0.03 | ≤0.03 |
75SiMn | 0.70-0.90 | 0.70-1.20 | 0.4-0.8 | ≤0.25 | ≤0.03 | ≤0.03 |
B2 | 0.70-0.85 | 0.70-0.80 | 0.17-0.37 | 0.2-0.7 | ≤0.035 | ≤0.035 |
B3 | 0.55-0.65 | 0.75-0.9 | 0.2-0.37 | 0.85-1.2 | ≤0.03 | ≤0.03 |
B4 | 0.58-0.66 | 0.65-0.80 | 1.6-1.9 | 0.7-0.9 | ≤0.03 | ≤0.03 |
B6 | 0.75-0.95 | 0.9-1.0 | 0.2-0.40 | 0.85-0.95 | ≤0.035 | ≤0.035 |
40Cr | 0.37-0.44 | 0.50-0.80 | 0.17-0.37 | 0.8-1.10 | ≤0.035 | ≤0.035 |
45# | 0.42-0.50 | 0.50-0.80 | 0.17-0.37 | ≤0.25 | ≤0.035 | ≤0.035 |
力学性能与金相组织
材质Material | 冲击值 落球次数 Ak（J/cm2） Falling Ball Times | 表面硬度 球心硬度 Surface（HRC） Core（HRC） | 金相组织 Microstructure |
50MN | ≥12 | ≥10000 | ≥56 | ≥48 | M+C |
60MN | ≥15 | ≥12000 | ≥58 | ≥50 | M+C |
65MN | ≥15 | ≥12000 | ≥60 | ≥50 | M+C |
75Mn | ≥17 | ≥12000 | ≥60 | ≥52 | M+C |
75MnCr | ≥16 | ≥12000 | ≥60 | ≥50 | M+C |
75SiMn | ≥17 | ≥12000 | ≥60 | ≥54 | M+C |
B2 | ≥15 | ≥12000 | ≥60 | ≥50 | M+C |
B3 | ≥12 | ≥10000 | ≥60 | ≥55 | M+C |
B4 | ≥12 | ≥12000 | ≥60 | ≥55 | M+C |
B6 | ≥15 | ≥12000 | ≥60 | ≥55 | M+C |
40Cr | ≥12 | ≥12000 | ≥60 | ≥55 | M+C |
45# | ≥12 | ≥10000 | ≥52 | ≥45 | M+C |
| M-马氏体 | Martensite | C -碳化物 | Carbide |
|
产品规格尺寸 | Size（mm） 公差 | Tolerance（mm） 单重 | Weight（kg/pc） 数量 | Quantity（pcs/ton） |
Φ20 |
+2 -1 | 0.032 | 31250 |
Φ25 | 0.064 | 15625 |
Φ30 | 0.11 | 9090 |
Φ40 | 0.263 | 3802 |
Φ50 | 0.513 | 1949 |
Φ60 |
+3
-2 | 0.888 | 1126 |
Φ70 | 1.41 | 709 |
Φ80 | 2.104 | 475 |
Φ90 | 2.996 | 333 |
Φ100 | 4.11 | 243 |
Φ110 |
+4
-2
| 5.457 | 182 |
Φ120 | 7.102 | 140 |
Φ130 | 9.03 | 110 |
Φ140
|
+4
-3
| 11.278 | 88 |
Φ150 |
13.871 |
72 |